  • Home > Welding Material > Welding Flux(SJ501)
  • Product Images
  • Welding Flux(SJ501)

  • detailed description
  • Welding flux(SJ501) Conforming to: GB/T5293 F4A0-H08A F5A2-H08MnA
    Welding flux(SJ501) Equivalent to: AWS-A5.17 F6A0-EL12 F7A2-EM12K DIN BAR 188AC 10KM
    Welding flux(SJ501) Description:
    SJ501is a kind of aluminum-titanium sintered flux, and its alkalinity is about 0.5 to 0.8,
    mesh 10-40(that is -l.7-0.38mm). Either alternating or direct current can be used. It is easy to
    deslag and the deposited metal has a fine property of rust resistance, and the welding bead is
    smooth while the welding performance is excellent.
    Welding flux(SJ501) Usage:
    When applied with different welding wires such as H08A, H08MnA, H08MnMo and
    H-l0MnSi, SJ501 can weld low-carbon steel, low-alloy steel and steel used for pressure vessels.
    And it is fit for fast welding of thin steel sheet like gas cylinders and membrane water-cooled
    wall in boiler factory.

    Compositions of fluxes(%)

    SiO2+TiO2

    Al2O3+MnO

    CaF2

    S

    P

    25-35

    50-60

    3-10

    ≤0.06

    ≤0.08

    Typical all weld metal mechanical property

    Wire matched

    Yield point

    σs (MPa)

    Tensile Strabgth

    σb(MPa)

    Elongation

    δ5(%)

    AKV(J)

    0

    -20

    H08A

    330

    415-550

    22

    50

    27

    H08MnA

    400

    480-650

    22

    50

    27

    EL12

    330

    415-550

    22

    --

    27

    EM12K

    400

    480-650

    22

    --

    27

    Welding flux(SJ501) Cautions:
    (1) The oil soil, moisture, iron rust and other foreign substances must be removed from the welding joint.
    (2) The welding flux must be baked under 300-350℃ for 2 hours before application.