ER4047
ER4047 Aluminum Welding Wire
item No: ER4047(AlSi12)
Typical composition(percent)
Si Fe Cu Mn Mg Zn Be Ti Others
11.00~13.00 ＜0.60 ＜0.30 ＜0.15 ＜0.10 ＜0.20 ＜0.0003 ＜0.15 ＜0.05
Physical properties(Approx. Values)
0.2percent yield strength Rp0.2(Mpa): 60
Tensile strength Rm(Mpa): 130
Elongation A5(L0=5d0)(percent): 5
Test temperature(℃): 20
Shielding gas: Argon, Helium or Argon/Helium-mixtures
Dimension
Mig wire(mm): 0.8, 0.9, 1.0, 1.2, 1.6, 2.0, 2.4
Tig rod(mm): 1.6, 2.0, 2.4, 3.2, 4.0, 5.0, 6.0
Wire Packaging
Mig wire: S100/0.5kg 11b, S200/2kg, S300/6-7kg 161b, S360/20kg
Tig Rod: 5/10kg Length 1000mm
CE cetificate
Si Fe Cu Mn Mg Zn Be Ti Others
11.00~13.00 ＜0.60 ＜0.30 ＜0.15 ＜0.10 ＜0.20 ＜0.0003 ＜0.15 ＜0.05
Physical properties(Approx. Values)
0.2percent yield strength Rp0.2(Mpa): 60
Tensile strength Rm(Mpa): 130
Elongation A5(L0=5d0)(percent): 5
Test temperature(℃): 20
Shielding gas: Argon, Helium or Argon/Helium-mixtures
Dimension
Mig wire(mm): 0.8, 0.9, 1.0, 1.2, 1.6, 2.0, 2.4
Tig rod(mm): 1.6, 2.0, 2.4, 3.2, 4.0, 5.0, 6.0
Wire Packaging
Mig wire: S100/0.5kg 11b, S200/2kg, S300/6-7kg 161b, S360/20kg
Tig Rod: 5/10kg Length 1000mm
CE cetificate
This is a type of aluminum alloys wire containing 12percent silicon, which can be adapted in welding all kinds of forging and casting or extruded shape aluminum alloys. And it has advantages of low melting point and good fluidity which avoides the distortion after selding.
Product usage: Jointing or overlay light alloy processing.