Mild Steel Flux Cored Welding Wire

item No: E71T-1
Chemical Composition of Deposited Metal(percent) 
  C             Mn          Si          P           S
≤0.18     ≤1.75     ≤0.90     ≤0.03     ≤0.03
Mechanical Properties of Deposited Metal
Rm(Mpa)    Rp(Mpa)    A5(percent)    Akv(J)(-20℃)
490~660       ≥400       ≥22           ≥27
Recommended Welding Parameter: DC(+)  Shielding Gas: Co2
Wire Diameter(mm)   Welding Current(A)   Welding Voltage(V)   Gas Flow(L/min)
         φ0.8                       50-100                       18-20                   15-25 
         φ0.9                       60-110                       18-20                   15-25
         φ1.0                       70-120                       19-21                   15-25 
         φ1.2                      140-300                       20-30                  15-25 
         φ1.4                      200-360                       24-32                  15-25 
         φ1.6                      240-380                       26-34                  15-25

Characteristics
Tianium oxide slag system, excellent welding performance, soft and stable arc, low spatter, good slag detachability and beautiful weld bead appearance; excellent machanical properties, high impact absorbing energy and lower diffusible hygrogen content, which is less than 5ml/100g.
Applications
Used for welding low carbon steel and low alloy high strength steel with 500Mpa grade: widly used for shipbuilding, bridge, constrction, storange tanks, boilers and various stee structure welding.